Strength of Partial-Joint-Penetration Groove Welds as Affected by Root Opening, Reinforcing, and Loading Direction
| 题名： | Strength of Partial-Joint-Penetration Groove Welds as Affected by Root Opening, Reinforcing, and Loading Direction |
| 正文语种： | 英文 |
| 作者： | Mathew Reynolds; Quang Huynh;Behzad Rafezy;Chia-Ming Uang, M.ASCE |
| 作者单位： | Univ, of California |
| 关键词： | Partial-joint penetration; Welding; Rein forced welds; Root opening; Load directio nality effect |
| 摘要： | Testing of 21 single-sided partial-joint-penetration (PJP) groove weld specimens was performed to evaluate the effects of three parameters: (1) root opening, (2) weld reinforcing profiles, and (3) directionality of loading. The specimens consisted of either 25-mm (1-in.) or 51-mm (2-in.) thick ASTM A572 Gr. 50 (345 MPa) steel plates welded in the shop with E70T-1C/9C electrodes using gas shielded flux-core arc welding (FCAW-G). Most of the specimens (18) were cruciform in shape and loaded the PJP groove weld in the transverse orientation. Three remaining specimens were orientated such that the PJP weld was loaded longitudinally. Most of the specimens (16 out of 21) failed through the PJP weld. The five remaining specimens failed in the plates or fillet welds outside of the tested PJP welds. The resulting failure load is then compared to the design equations of AISC 360, The observation that the reinforcing fillet did not enhance the strength of the PJP-welded joint is explained by the transition of the tensile fracture surface to shear fracture surface. |
| 出版日期： | 2020 |
| 出版年： | 2020 |
| 期刊名称： | Journal of Structural Engineering |
| 卷： | Vol.146 |
| 期： | No.08 |
| 页码： | 04020150 |
相关文献
- Directionality Effect on Strength of Partial-Joint-Penetration Groove Weld Joints
- Weld Effective Lengths for Axially Loaded Transverse Plate-to-CHS Connections
- Simulation-Based Fracture Assessment of Seismic Moment Frame Connections with Box Columns
- Prying Models for Strength in Thick-Flange Built-Up T-Stubs with Complete Joint Penetration and Fillet Welds
- Fracture Mechanics-Based Design of Column Splices with Partial Joint Penetration Welds
- Fracture Mechanics–Based Fragility Assessment of Pre-Northridge Welded Column Splices
检索历史
应用推荐