LONG-TERM OVEN-AGING EFFECTS ON FATIGUE AND INITIAL STIFFNESS OF ASPHALT CONCRETE.
| 题名： | LONG-TERM OVEN-AGING EFFECTS ON FATIGUE AND INITIAL STIFFNESS OF ASPHALT CONCRETE. |
| 作者： | Harvey-J; Tsai-B-W |
| 关键词： | ASPHALT-CONCRETE; LONG-TERM-OVEN-AGING; STIFFNESS-; FATIGUE-MATERIALS; ASPHALT-CONTENT; AIR-VOIDS-CONTENT; BEAM-TESTS; STRATEGIC-HIGHWAY-RESEARCH-PROGRAM; FATIGUE-LIFE |
| 摘要： | An investigation of the effects of long-term oven aging (LTOA) on initial stiffness and fatigue of asphalt concrete was made using two typical California asphalts, known to have different aging characteristics, in mixes with one aggregate. Asphalt content, air-voids content, and days of LTOA were varied independently. Stiffness and fatigue were evaluated using the controlled-strain flexural beam test developed by the Strategic Highway Research Program Project A-003A. The results indicated that both mixes exhibited an increase in initial stiffness with LTOA periods of up to six days. The sensitivity of beam fatigue life to LTOA depended on the asphalt. Beams containing Valley asphalt had virtually no change in fatigue life due to LTOA, whereas beams with Coastal asphalt showed some sensitivity to LTOA. For both asphalts, the average reduction in fatigue life from 6 days of LTOA was less than that caused by a 3% increase in air-void content or a 1% decrease in asphalt content. Simulations of thick and thin pavement structures were performed to reconcile the effects of LTOA, asphalt content, and air-void content on mix fatigue life and stiffness by evaluating their combined effects on predicted pavement fatigue life. The simulations indicated that aging, as induced by LTOA, increased fatigue life for all cases except one. |
| 总页数： | Transportation Research Record. 1997. (1590) pp89-98 (4 Fig., 5 Tab., 10 Ref.) |
| 报告类型： | 科技报告 |
相关文献
- EFFECT OF HYDRATED LIME ON LONG-TERM OXIDATIVE AGING CHARACTERISTICS OF ASPHALT.
- EFFECTS OF ASPHALT CONTENT AND AIR VOID CONTENT ON MIX FATIGUE AND STIFFNESS.
- Initial Development of a Calibrated Mechanistic Approach and Associated Surrogate Test Protocols for HMAC Mixture Fatigue Characterization.
- EFFECT OF SEGREGATION ON FATIGUE PERFORMANCE OF ASPHALT PAVING MIXTURES.
- Fatigue Behavior of Rubber-Modified Pavements
- ENERGY-DERIVED, DAMAGE-BASED FAILURE CRITERION FOR FATIGUE TESTING.
检索历史
应用推荐