Investigation into Shrinkage of High Performance Concrete Used for Iowa Bridge Decks and Overlays - Phase II Shrinkage Control and Field Investigation TR-690 (Phase II for TR-663)
| 项目名称： | Investigation into Shrinkage of High Performance Concrete Used for Iowa Bridge Decks and Overlays - Phase II Shrinkage Control and Field Investigation TR-690 (Phase II for TR-663) |
| 摘要： | High performance concrete (HPC) is increasingly used in bridge deck and deck overlays because of its high strength, low permeability and excellent durability. However, due to its high cementitious content, low water-to-binder ratio (w/b) and use of various admixtures, HPC can have a high risk for shrinkage cracking. Cracks weaken structures and permit water and harmful chemical ingress into concrete, thereby accelerating deterioration and corrosion of reinforcement (Shah et al 1997). Shrinkage also causes concrete slab to curl and warp, which affects the girder-to-deck composite action, ultimately decreasing load-carrying capacity of the bridge (Tarr 2008). In addition, shrinkage may bring about stress loss in prestressed concrete structures and affect camber and deflection and load carrying capacity of bridge girders. Over the past decade, many states have reported cracking on HPC bridge decks at early ages (Wan 2010 and Whiting et al 2000), and this problem is also a great concern in Iowa. Recently, the Iowa Highway Research Board (IHRB) has sponsored a Project TR-633, Investigation into Shrinkage of High Performance Concrete Used for Iowa Bridge Decks and Overlays (Phase I). In this study, autogenous, free drying, and restrained ring shrinkage of 11 typical Iowa HPC mixes were monitored over time. The mechanical properties (such as elastic modulus and compressive and splitting tensile strength), creep coefficients, and cracking potentials of these concrete mixes were evaluated. The results indicated that among these 11 mixes studied, three mixes were identified as having high cracking potential and five mixes as having medium cracking potential. The researchers have suggested that the shrinkage behavior of the mixes identified as having high cracking potential could be modified by using the state-of-the art shrinkage reduction and control technologies, such as use of shrinkage-reducing agents (SRA), shrinkage compensating admixture (SCA) and internal curing (IC). The shrinkage behavior of the mixes identified as having medium cracking potential can be tailored through the balance between the w/b, cementitious content, and tensile strength. A field study shall be conducted to monitor and compare the performance of the high and low shrinkage cracking mixes used in Iowa. To verify and implement the research results obtained from the Phase I study of Project TR633, a Phase II study as proposed as below is to further investigate and identify the most functional, practical and cost effective method for controlling shrinkage cracking potential of HPC in Iowa bridge decks and overlays. |
| 状态： | Completed |
| 资金： | 299993.00 |
| 资助组织： | Iowa Department of Transportation |
| 项目负责人： | Goetz, Vanessa |
| 执行机构： | Iowa State University, Ames |
| 主要研究人员： | Wang, Kejin |
| 开始时间： | 20150701 |
| 预计完成日期： | 20190228 |
| 实际结束时间： | 0 |
相关文献
- Review and Specification for Shrinkage Cracks of Bridge Decks, Phase II
- Bridge Deck Overlays Using Ultra-High Performance Concrete
- Reducing Shrinkage in Concrete Bridge Decks using Single and Double Ring Test Methods
- Low-Cost Rural Surface Alternatives Phase III: Demonstration Project TR-721
- 2260 - Shrinkage Induced Deformation in Steel Bridges Made Composite with Concrete Deck Slabs - Phase 3
- Structural Health Monitoring to Determine Long-Term Behavior of AFRP Composite Bars in Prestressed Concrete Panels for Field Deployment
检索历史
应用推荐