Study of Near-Threshold Fatigue Crack Propagation in Pipeline Steels in High Pressure Environments
| 题名： | Study of Near-Threshold Fatigue Crack Propagation in Pipeline Steels in High Pressure Environments |
| 作者： | Mitchell, M. |
| 关键词： | threshold；pressure；pipeline；environment；fatigue；pagat；study；crac；eels；stee |
| 摘要： | Near threshold fatigue crack propagation in pipeline steels in high pressure environments was studied. The objective was to determine the level of threshold stress intensity for fatigue crack growth rate behavior in a high strength low alloy X60 pipeline-type steel. Complete results have been generated for gaseous hydrogen at ambient pressure, laboratory air at ambient pressure and approximately 60%relative humidity as well as vacuum of 0.000067 Pa ( 0.0000005 torr) at R-ratios = K(min)/K(max) of 0.1, 0.5, and 0.8. Fatigue crack growth rate behavior in gaseous hydrogen, methane, and methane plus 10 percent hydrogen at 6.89 MPa (100 psi) was determined. |
| 报告类型： | 科技报告 |
相关文献
- Effect of Ethanol Fuel and Microbiologically Influenced Corrosion on the Fatigue Crack Growth Behavior of Pipeline Steels.
- Effect of Ethanol Fuel and Microbiologically Influenced Corrosion on the Fatigue Crack Growth Behavior of Pipeline Steels
- Experimental and Finite Element Modeling of Near-Threshold Fatigue Crack Growth for the K-Decreasing Test Method.
- Abrupt Transition to an Intergranular Failure Mode in the Near-Threshold FCG Regime in Ni-Based Superalloys [STUB].
- Developing Fatigue Pre-crack Procedure to Evaluate Fracture Toughness of Pipeline Steels Using Spiral Notch Torsion Test.
- Fatigue Design 1998. Volume 2. (Conference) Held in Espoo, Finland on May 26-29, 1998
检索历史
应用推荐