原文传递 Test and Analysis Correlation for a Y-Joint Specimen for a Composite Cryotank.

题名：	Test and Analysis Correlation for a Y-Joint Specimen for a Composite Cryotank.
作者：	Mason, B. H.; Sleight, D. W.; Grenoble, R.
关键词：	Cryogenic tanks, Composite materials, Fracture mechanics, Laminates, Shear stress, Far fields, Strain gages, Thermal expansion, Delaminating, Elastic properties, Crack initiation, Structural analysis, Failure modes, Strain measurement, Low temperature tests, Finite element method
摘要：	The Composite Cryotank Technology Demonstration (CCTD) project under NASA's Game Changing Development Program (GCDP) developed space technologies using advanced composite materials. Under CCTD, NASA funded the Boeing Company to design and test a number of element-level joint specimens as a precursor to a 2.4-m diameter composite cryotank. Preliminary analyses indicated that the y-joint in the cryotank had low margins of safety; hence the y-joint was considered to be a critical design region. The y-joint design includes a softening strip wedge to reduce localized shear stresses at the skirt/dome interface. In this paper, NASA-developed analytical models will be correlated with the experimental results of a series of positive-peel y-joint specimens from Boeing tests. Initial analytical models over-predicted the experimental strain gage readings in the far-field region by approximately 10%. The over-prediction was attributed to uncertainty in the elastic properties of the laminate and a mismatch between the thermal expansion of the strain gages and the laminate. The elastic properties of the analytical model were adjusted to account for the strain gage differences. The experimental strain gages also indicated a large non-linear effect in the softening strip region that was not predicted by the analytical model. This non-linear effect was attributed to delamination initiating in the softening strip region at below 20% of the failure load for the specimen. Because the specimen was contained in a thermally insulated box during cryogenic testing to failure, delamination initiation and progression was not visualized during the test. Several possible failure initiation locations were investigated, and a most likely failure scenario was determined that correlated well with the experimental data. The most likely failure scenario corresponded to damage initiating in the softening strip and delamination extending to the grips at final failure.
总页数：	Mason, B. H.; Sleight, D. W.; Grenoble, R.
报告类型：	科技报告