Electrochemical Aging of Thermal-Sprayed Zinc Anodes on Concrete.
| 题名： | Electrochemical Aging of Thermal-Sprayed Zinc Anodes on Concrete. |
| 作者： | McGill, G.E.;Cryer, C.B.;Cramer, S.D.;Covino, B.S. Jr.;Bullard, S.J.;Holcomb, G.R.; |
| 关键词： | *Concrete-structures; *Zinc-coatings; *Aging-; *Electrochemical-corrosion.;Bridges-; Cathodic-protection; Concretes-; Cements-; Coatings-. |
| 摘要： | Thermal-sprayed zinc anodes are used in impressed current cathodic protection systems for some of Oregon's coastal reinforced concrete bridges. Electrochemical aging of zinc anodes results in physical and chemical changes at the zinc-concrete interface. Concrete surfaces heated prior to thermal-spraying had initial adhesion strengths 80 pct higher than unheated surfaces. For electrochemical aging greater than 200 kC/m(sup 2) (5.2 A h/ft(sup 2)), there was no difference in adhesion strengths for zinc on preheated and unheated concrete. Adhesion strengths decreased monotonically after about 400 to 600 kC/m(sup 2) (10.4 to 15.6 A-h/ft(sup 2)) as a result of the reaction zones at the zinc-concrete interface. A zone adjacent to the metallic zinc (and originally part of the zinc coating) was primarily zincite (ZnO), with minor constituents of wulfingite (Zn(OH)(sub 2)), simonkolleite (Zn(sub 5)(OH)(sub 8)C(sub l2)(sup .)H(sub 2)O), and hydrated zinc hydroxide sulfates (Zn(sub 4)SO(sub 4)(OH)(sub 6)(sup .)xH(sub 2)O). This zone is the locus for cohesive fracture when the zinc coating separates from the concrete during adhesion tests. Zinc ions substitute for calcium in the cement paste adjacent to the coating as the result of secondary mineralization. The initial estimate of the coating service life based on adhesion strength measurements in accelerated impressed current cathodic protection tests is about 27 years. |
| 报告类型： | 科技报告 |
相关文献
- SPRAYED ZINC GALVANIC ANODES FOR CONCRETE MARINE BRIDGE SUBSTRUCTURES.
- FIELD APPLICATION OF A THERMAL-SPRAYED TITANIUM ANODE FOR CATHODIC PROTECTION OF REINFORCING STEEL IN CONCRETE.
- EVALUATION OF ANODES FOR GALVANIC CATHODIC PREVENTION OF STEEL CORROSION IN PRESTRESSED CONCRETE PILES IN MARINE ENVIRONMENTS IN VIRGINIA
- Evaluation of Anodes for Galvanic Cathodic Prevention of Steel Corrosion in Prestressed Concrete Piles in Marine Environments in Virginia; Final rept. 1996.10-Jun 99
- GALVANIC CATHODIC PROTECTION OF REINFORCED CONCRETE BRIDGE MEMBERS USING SACPJnCIAL ANODES ATTACHED BY CONDUCTIVE ADHESIVES
- IDENTIFICATION OF CHEMICAL AGENTS FOR THE CONTROL OF ALKALI-AGGREGATE REACTION IN CONCRETE.
检索历史
应用推荐