原文传递 Destructive Examination of Shipping Package 9975-06100

题名：	Destructive Examination of Shipping Package 9975-06100
作者：	Daugherty, W. L.
关键词：	Shipping containers##Packaging##Air##Corrosion##Degradation##Fiberboards##Lead##Moisture##Shields##Stainless steels##
摘要：	Destructive and non-destructive examinations have been performed on specified components of shipping package 9975-06100. This package was selected for examination based on several characteristics: - This was the first destructively examined package in which the fiberboard assembly was fabricated from softwood fiberboard. - The package contained a relatively high heat load to contribute to internal temperature, which is a key environmental factor for fiberboard degradation. - The package has been stored in the middle or top of a storage array since its receipt in K- Area, positions that would contribute to increased service temperatures. No significant changes were observed for attributes that were measured during both field surveillance and destructive examination. Except for the axial gap, all observations and test results met identified criteria, or were collected for information and trending purposes. The axial gap met the 1 inch maximum criterion during field surveillance, but was just over the criterion during SRNL measurements. When re-measured at a later date, it again met the criterion. The bottom of the lower fiberboard assembly and the drum interior had two small stains at matching locations, suggestive of water intrusion. However, the fiberboard assembly did not contain any current evidence of excess moisture. No evidence of a degraded condition was found in this package. Despite exposure to the elevated temperatures of this higher-then-average wattage package, properties of the fiberboard and O-rings are consistent with those of new packages.
总页数：	36
报告类型：	科技报告