Numerical Modeling of Nonuniform Corrosion-Induced Concrete Crack Width
| 题名： | Numerical Modeling of Nonuniform Corrosion-Induced Concrete Crack Width |
| 其他题名： | Rabczuk,T.,G.Zi,S.Bordas,and H.Nguyen-Xuan.2010."A simple and robust three-dimensional cracking-particle method without enrichment."Comput.Methods Appl.Mech.Eng.199(37-40):2437-2455.https://doi.org/10.1016/j.cma.2010.03.031. |
| 正文语种： | 英文 |
| 作者： | Shangtong Yang |
| 关键词： | Corrosion;Crack width;Cohesive crack model;Reinforced concrete;Numerical modeling |
| 摘要： | Corrosion of reinforced concrete is one of the major deterioration mechanisms that results in premature failure of the reinforced concrete structures. In practice, concrete crack width is one of the most important criteria for the assessment of the serviceability of concrete structures. Literature review suggests that little research has been undertaken on numerical prediction of concrete crack width, especially by considering the corrosion as a nonuniform process. This paper attempts to develop a numerical model to predict concrete crack width for corrosion-affected concrete structures under realistic nonuniform corrosion of the reinforcement. A nonuniform corrosion model was first formulated as a function of time. To simulate arbitrary cracking in concrete, cohesive elements are inserted in the sufficiently fine mesh that is achieved through a script written in Python. The surface crack width is obtained as a function of service time, and verification against experimental results from literature is conducted. Accurate prediction of crack width can allow timely maintenance, which prolongs the service life of the reinforced concrete structures. |
| 出版年： | 2018 |
| 论文唯一标识： | P-26Y2018V144N08029 |
| 英文栏目名称： | TECHNICAL PAPERS |
| doi： | 10.1061/(ASCE)ST.1943-541X.0002108 |
| 期刊名称： | Journal of Structural Engineering |
| 拼音刊名(出版物代码)： | P-26 |
| 卷： | 144 |
| 期： | 08 |
| 页码： | 357-368 |
相关文献
- Machine Learning–Based Reliability Analysis of Structural Concrete Cracking Considering Realistic Nonuniform Corrosion Development
- Epoxy Injection for Cracked Concrete
- Prediction of Time to Corrosion-Induced Concrete Cracking Based on Fracture Mechanics Criteria
- Residual Flexural Capacity and Performance Assessment of Corroded Reinforced Concrete Beams
- Prestress Loss Diagnostics in Pretensioned Concrete Structures with Corrosive Cracking
- Analytical Evaluation of Corrosion-Induced Strength Degradation in Prestressed Bridge Girders
检索历史
应用推荐