DURABILITY EVALUATION OF CONCRETE CRACK REPAIR SYSTEMS.
| 题名： | DURABILITY EVALUATION OF CONCRETE CRACK REPAIR SYSTEMS. |
| 作者： | Tsiatas-G; Robinson-J |
| 关键词： | Beams-; Cement-; Concrete-bridges; Crack-width; Cracking-; Durability-; Epoxy-resins; Fatigue-tests; Freeze-thaw-tests; High-molecular-weight-methacrylate; Materials-; Repairing- |
| 摘要： | Concrete cracking in highway bridges is a major problem because it not only accelerates the rate of deterioration, but it also can reduce the structural strength of the bridge. Crack repair systems have been developed to address this problem. For repairing structural cracks, six repair materials were evaluated for durability. The repair materials include one cementitious system, one modified cementitious system, two epoxy-based systems, and two high-molecular-weight methacrylate (HMWM) repair products. Each product was applied according to its manufacturer's directions to repair beams with crack widths of 0.51 mm (0.02 in.), 6.35 mm (0.25 in.), and 12.70 mm (0.50 in.). The specimens are subjected to a standard freezing and thawing test followed by fatigue testing to failure. In general, epoxies and HMWMs performed the best. However, individual products varied significantly. Specimens repaired with the cementitious system were unable to resist any significant amount of fatigue-loading cycles. |
| 总页数： | Transportation Research Record. 2002. (1795) pp82-87 (1 Phot., 2 Fig., 2 Tab., 5 Ref.) |
| 报告类型： | 科技报告 |
相关文献
- Evaluation of Conventional Repair Techniques for Concrete Bridges
- RUBBLIZATION OF CONCRETE PAVEMENTS: FIELD INVESTIGATION.
- INNOVATIVE MATERIALS AND EQUIPMENT FOR PAVEMENT SURFACE REPAIRS. VOLUME III: DATA BASE USERS GUIDE.
- Durability and Bond of High Performance Concrete and Repaired Portland Cement Concrete; Final rept
- Preformed Silicon Bridge Deck Joint Sealing System
- INNOVATIVE MATERIALS AND EQUIPMENTS FOR PAVEMENT SURFACE REPAIRS. VOLUME II: SYNTHESIS OF OPERATIONAL DEFICIENCIES OF EQUIPMENT USED FOR PAVEMENT SURFACE REPAIRS.
检索历史
应用推荐