MECHANICAL TESTING OF CARBON STEEL IN HIGH PRESSURE HYDROGEN
| 题名： | MECHANICAL TESTING OF CARBON STEEL IN HIGH PRESSURE HYDROGEN |
| 作者： | Duncan, A; |
| 关键词： | 36 MATERIALS SCIENCE; 03 NATURAL GAS; 08 HYDROGEN; CARBON STEELS; CLEAVAGE; CONSTRUCTION; FRACTURES; HEAT AFFECTED ZONE; HYDROGEN; MECHANICAL PROPERTIES; MECHANICAL TESTS; NATURAL GAS; PIPELINES; RUPTURES; SERVICE LIFE; STEELS; TENSILE PROPERTIES; TESTING |
| 摘要： | The methods and interim results from a testing program to quantify hydrogen effects on mechanical properties of carbon steel pipeline and pipeline weld materials are provided. The scope is carbon steels commonly used for natural gas pipelines in the United States that are candidates for hydrogen service in the hydrogen economy. The mechanical test results will be applied in future analyses to evaluate service life of the pipelines. The results are also envisioned to be part of the bases for construction codes and structural integrity demonstrations for hydrogen service pipeline and vessels. Tensile properties of one type of steel (A106 Grade B) in base metal, welded and heat affected zone conditions were tested at room temperature in air and high pressure (1500 psig) hydrogen. A general reduction in the materials ability to plastically deform was noted in this material when specimens were tested in 1500 psig hydrogen. Furthermore, the primary mode of fracture was changed from ductile rupture in air to cleavage with secondary tearing in hydrogen. The mechanical test program will continue with tests to quantify the fracture behavior in terms of J-R curves for these materials at air and hydrogen pressure conditions. |
| 报告类型： | 科技报告 |
相关文献
- TENSILE TESTING OF CARBON STEEL IN HIGH PRESSURE HYDROGEN
- Multi-fuel reformers for fuel cells used in transportation: Assessment of hydrogen storage technologies. Phase 2: Final report
- Mechanical Properties of Additively Manufactured Stainless Steel.
- Developing Fatigue Pre-crack Procedure to Evaluate Fracture Toughness of Pipeline Steels Using Spiral Notch Torsion Test.
- Study of Near-Threshold Fatigue Crack Propagation in Pipeline Steels in High Pressure Environments
- Material Solutions for Hydrogen Delivery in Pipelines. Final Report.
检索历史
应用推荐