The Effect of Cathodic Protection on Stress Corrosion Cracking of High-Strength Pipeline Steels
| 项目名称： | The Effect of Cathodic Protection on Stress Corrosion Cracking of High-Strength Pipeline Steels |
| 摘要： | The objective of this project is to establish the effectiveness of cathodic protection in mitigating stress corrosion cracking (without causing hydrogen damage) for a range of high-strength pipeline steels from X-70 to X-120, and to assess the effects of overprotection and underprotection. |
| 状态： | Completed |
| 资金： | 60700.00 |
| 资助组织： | Pipeline and Hazardous Materials Safety Administration |
| 项目负责人： | Katchmar, Peter |
| 执行机构： | CANMET Materials Technology Laboratory |
| 开始时间： | 20080601 |
| 实际结束时间： | 20091202 |
| 主题领域： | Maintenance and Preservation；Pipelines |
相关文献
- In-Situ Hydrogen Analysis in Weldments: Novel NDE for Weld Inspection
- Consolidated Project Full Scale Testing of Interactive Features for Improved Models
- Effect of Concentration and Temperature of Ethanol in Fuel Blends on Microbial and Stress Corrosion Cracking of Pipeline Steels
- LONG-TERM TESTS ON THE ACTION OF CHLORIDE ON THE CORROSION OF PRESTRESSING STEELS IN CONCRETE
- Model Modules to Assist Assessing and Controlling Stress Corrosion Cracking (SCC)
- Development of a Commercial Model to Predict Stress Corrosion Cracking Growth Rates in Operating Pipelines
检索历史
应用推荐